430 stainless steel sheet
| C% | Si% |
Mn% |
P% |
S% |
Cr% |
Ni% |
N% |
Mo% |
Ti% |
≤0.12 |
≤1.00 |
≤1.00 |
≤0.040 |
≤0.030 |
16.0-18.0 |
≤0.75 |
-- |
-- |
-- |
T*S |
Y*S |
Hardness |
Elongation |
|
(Mpa) |
(Mpa) |
HRB |
HB |
(%) |
≥520 |
≥205 |
-- |
-- |
≥40 |
Cold Rolled 430 stainless steel sheet
1. Grade: 200 & 300 series
200 seriers: 201,202, J4
300 seriers: 301, 304, 304L, 321, 316L, 309, 310S
2. Standard: JIS, ASTM, AISI, GB, DIN, EN, we usually use ASTM and GB Standard
3. Thickness: 0.14mm-3.0mm
4. Width: as require
5. Surface: 2B finished, BA finished
6. Hardness: soft, 1/4H, 1/2H, FH
7. Thickness Tolerance: +/-0.02mm
8. Width Tolerance: +/-10mm(mill edge)
More grades of 430 ss sheet
Type |
Grade |
Grade |
Chemical Component % |
||||
Austenitic stainless steel |
C |
Cr |
Ni |
Mn |
|||
201 |
1Cr17Mn6Ni5N |
≤0.15 |
16.00-18.00 |
3.50-5.50 |
5.50－7.50 |
||
201L |
03Cr17Mn6Ni5N |
≤0.030 |
16.00-18.00 |
3.50-5.50 |
5.50－7.50 |
||
202 |
1Cr18Mn8Ni5N |
≤0.15 |
17.00-19.00 |
4.00-6.00 |
7.50-10.00 |
||
204 |
03Cr16Mn8Ni2N |
≤0.030 |
15.00-17.00 |
1.50-3.50 |
7.00-9.00 |
||
1Cr18Mn10Ni5Mo3N |
≤0.10 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
|||
2Cr13Mn9Ni4 |
0.15-0.25 |
12.00-14.00 |
3.70-5.00 |
8.00-10.00 |
|||
2Cr15Mn15Ni2N |
0.15-0.25 |
14.00-16.00 |
1.50-3.00 |
14.00-16.00 |
|||
1Cr18Mn10Ni5Mo3N |
≤0.15 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
|||
301 |
1Cr17Ni7 |
≤0.15 |
16.00-18.00 |
6.00-8.00 |
≤2.00 |
||
302 |
1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
303 |
Y1Cr18Ni9 |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
303se |
Y1Cr18Ni9Se |
≤0.15 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
304 |
0Cr18Ni9 |
≤0.07 |
17.00-19.00 |
8.00-10.00 |
≤2.00 |
||
304L |
00Cr19Ni10 |
≤0.030 |
18.00-20.00 |
8.00-10.00 |
≤2.00 |
||
304N1 |
0Cr19Ni9N |
≤0.08 |
18.00-20.00 |
7.00-10.50 |
≤2.00 |
||
304N2 |
0Cr18Ni10NbN |
≤0.08 |
18.00-20.00 |
7.50-10.50 |
≤2.00 |
||
304LN |
00Cr18Ni10N |
≤0.030 |
17.00-19.00 |
8.50-11.50 |
≤2.00 |
||
305 |
1Cr18Ni12 |
≤0.12 |
17.00-19.00 |
10.50-13.00 |
≤2.00 |
||
309S |
0Cr23Ni13 |
≤0.08 |
22.00-24.00 |
12.00-15.00 |
≤2.00 |
||
310S |
0Cr25Ni20 |
≤0.08 |
24.00-26.00 |
19.00-22.00 |
≤2.00 |
||
316 |
0Cr17Ni12Mo2 |
≤0.08 |
16.00-18.50 |
10.00-14.00 |
≤2.00 |
||
1Cr18Ni12Mo2Ti6) |
≤0.12 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
0Cr18Ni12Mo2Ti |
≤0.08 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
316L |
00Cr17Ni14Mo2 |
≤0.030 |
16.00-18.00 |
12.00-15.00 |
≤2.00 |
||
316N |
0Cr17Ni12Mo2N |
≤0.08 |
16.00-18.00 |
10.00-14.00 |
≤2.00 |
||
316N |
00Cr17Ni13Mo2N |
≤0.030 |
16.00-18.50 |
10.50-14.50 |
≤2.00 |
||
316J1 |
0Cr18Ni12Mo2Cu2 |
≤0.08 |
17.00-19.00 |
10.00-14.50 |
≤2.00 |
||
316J1L |
00Cr18Ni14Mo2Cu2 |
≤0.030 |
17.00-19.00 |
12.00-16.00 |
≤2.00 |
||
317 |
0Cr19Ni13Mo3 |
≤0.12 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
||
317L |
00Cr19Ni13Mo3 |
≤0.08 |
18.00-20.00 |
11.00-15.00 |
≤2.00 |
||
1Cr18Ni12Mo3Ti6 |
≤0.12 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
0Cr18Ni12Mo3Ti |
≤0.08 |
16.00-19.00 |
11.00-14.00 |
≤2.00 |
|||
317J1 |
0Cr18Ni16Mo5 |
≤0.040 |
16.00-19.00 |
15.00-17.00 |
≤2.00 |
||
321 |
1Cr18Ni9Ti6 |
≤0.12 |
17.00-19.00 |
8.00-11.00 |
≤2.00 |
||
0Cr18Ni10Ti |
≤0.08 |
17.00-19.00 |
9.00-12.00 |
≤2.00 |
|||
347 |
0Cr18Ni11Nb |
≤0.08 |
17.00-19.00 |
9.00-13.00 |
≤2.00 |
||
XM7 |
0Cr18Ni9Cu3 |
≤0.08 |
17.00-19.00 |
8.50-10.50 |
≤2.00 |
||
XM15J1 |
0Cr18Ni13Si4 |
≤0.08 |
15.00-20.00 |
11.50-15.00 |
≤2.00 |
||
Austenite |
329J1 |
0Cr26Ni5Mo2 |
≤0.08 |
23.00-28.00 |
3.00-6.00 |
≤1.50 |
≤0.035 |
≤0.030 |
1.00-3.00 |
≤1.00 |
- |
- |
2) |
1Cr18Ni11Si4AlTi |
0.10-0.18 |
17.50-19.50 |
10.--120.. |
≤0.80 |
≤0.035 |
≤0.030 |
- |
3.40-4.00 |
- |
- |
Al 0.10-0.30; Ti 0.40-0.70 |
||
00Cr18Ni5MoSi2 |
≤0.030 |
18.00-19.50 |
4.50-5.50 |
1.00-2.00 |
≤0.035 |
≤0.030 |
2.50-3.00 |
1.30-2.00 |
- |
- |
- |
||
Ferrite Stainless Steel |
405 |
0Cr13Al |
≤0.08 |
11.50-14.50 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
Al 0.10-0.30 |
410L |
00Cr12 |
≤0.030 |
11.00-13.00 |
3) |
≤1.00 |
≤0.035 |
≤0.030 |
- |
≤1.00 |
- |
- |
- |
430 |
1Cr17 |
≤0.12 |
16.00-18.00 |
3) |
≤1.25 |
≤0.035 |
≤0.030 |
- |
≤0.75 |
- |
- |
- |
|
430F |
Y1Cr17 |
≤0.12 |
16.00-18.00 |
3) |
≤1.00 |
≤0.035 |
≥0.15 |
1) |
≤1.00 |
- |
- |
- |
|
434 |
1Cr17Mo |
≤0.12 |
16.00-18.00 |
3) |
≤1.00 |